Copper, DHP, Phosphorus-Deoxidized, High Residual Phosphorus. Deoxidization gives improved embrittlement resistance during welding. Has conductivity 85% IACS.
Applications
Used for electromechanical hardware connectors, bus bars, etc., where welding is required.
Machinability
The machinability rating of this alloy is 20. (Where Alloy 360 FC Brass is 100).
Welding
Soldering is rated as "excellent", brazing is rated as "excellent", oxyacetylene welding is rated as "good", gas shielded arc welding is rated as "excellent", coated metal arc welding is "not recommended", spot welding is "not recommended", seam welding is "not recommended" and butt welding is rated as "good".
Forging
The hot forgeability rating of this alloy is 65. (Forging brass = 100). The recommended hot working temperature for this alloy is between 1400 and 1600 F.
Hot Working
This alloy's capacity for being hot formed is rated as "excellent".
Cold Working
The capacity for cold working this alloy is rated as "excellent".
Annealing
The annealing temperature for this alloy is between 700 and 1200 F.
Physical Data
Density (lb / cu. in.)
0.323
Electrical Resistivity (microhm-cm (at 68 Deg F))
12.2
Mean Coeff Thermal Expansion
9.4
Modulus of Elasticity Tension
17000
Mechanical Data
MSO currently has no data available for this grade.
Disclaimer
This information is provided "as is" and Metal Suppliers Online, LLC makes no warranty of any kind with respect to the subject matter or accuracy of the information contained herein. Metal Suppliers Online, Inc. specifically disclaims all warranties, expressed, implied or otherwise, including without limitation, all warranties of merchantability and fitness for a particular purpose.
In no event shall Metal Suppliers Online, Inc. be liable for any special, incidental, indirect or consequential damages of any kind or any damages whatsoever resulting from loss of use, data, profits, whether or not advised of the possibility of damage, and on any theory of liability, arising out of or in connection with the use of the information contained herein.
This publication may include technical inaccuracies or typographical errors. Changes may be periodically made to the information herein.